The PET White film sticker is specially made for use on pressure tyres. Also called vulcanized label. The PET film is 125 micron thick and is heat stabilized to withstand pressure. The adhesive is also specific to this application. Thanks to its smooth surface, the print quality is at the highest level. Transparent PET film is used as the back scraper. The maximum heat resistance is 200 °C, during the vulcanization time this value increases to 220 °C.

PP opaque barrel rubber label or polypropylene label is one of the group of plastic-based labels. Produced in white color and is a label product that is extremely resistant to water, tearing and outdoor conditions. Opaque polypropylene does not stretch and does not tear easily as long as it is not forced. Because of these features, it is one of the types of labels that are suitable for use in outdoor environments, such as other plastic-based labels. It is long-lasting and also has a wide range of applications. They can be produced in printed form, and in addition, after they are produced, they can be printed with barcode printers using ribbon.

The PET White film sticker is specially made for use on pressure tyres. Also called vulcanized label. The PET film is 125 micron thick and is heat stabilized to withstand pressure. The adhesive is also specific to this application. Thanks to its smooth surface, the print quality is at the highest level. Transparent PET film is used as the back scraper. The maximum heat resistance is 200 °C, during the vulcanization time this value increases to 220 °C.

Adhesive adherence is difficult on silicone surfaces, and it is used on increased silicone fabrics used for mattresses to be soft. This makes it difficult for the label to adhere. This special transfer PET white film sticker is made to solve this problem. Solvent-based silicone adhesive was used as the adhesive type. It gives excellent results on textured, siliconized and low energy surfaces. It has superior resistance to extreme temperatures, humidity, chemicals and UV light. PET75 transparent film is used as the back scraper. It can be applied at a minimum of +5 °C and maintains its adhesive strength between -80 °C and +150 °C.

The transfer PET film sticker is specially manufactured to be resistant to heavy chemicals. If the appropriate resin is used with ribbon, the printing resistance is clear and permanent. Top surface is 56 µm PET film. It has a high immediate adhesion value and adhesive durability. White siliconized paper is used as the back scraper. Total thickness 146 µm (±10% ISO 534). The adhesive maintains its value between -40 °C to 150 °C and can be applied at a minimum of 7 °C.

The top surface of this label, which is suitable for thermal transfer printing and is permanently printed when resin is used with ribbon, has a 50 µm white glossy PET film on the upper surface. Two-sided siliconized white paper is used as the back scraper. Although the scraper paper is thin, it is quite hard and durable. The adhesive type is a special formulation called RHA (Rubber Hybridized Acrylic) to give excellent performance on rough and low energy surfaces. Thanks to this feature, it is suitable for use on rough barrels and other indented, uneven surfaces.

The top surface of this label, which is suitable for thermal transfer printing and is permanently printed when resin is used with ribbon, has a 50 µm white glossy PET film on the upper surface. Two-sided siliconized white paper is used as the back scraper. Although the scraper paper is thin, it is quite hard and durable. The adhesive type is a special formulation called RHA (Rubber Hybridized Acrylic) to give excellent performance on rough and low energy surfaces. Thanks to this feature, it is suitable for use on rough barrels and other indented, uneven surfaces.

The upper surface of the PET white film label is white PET film and the adhesive is heat stabilized acrylic adhesive. This adhesive is resistant to temperature and humidity. The application temperature is 5°C and it is resistant between -40 °C and + 220 °C. Silicon paper with a thickness of 68 µm was used as the back scraper. Ideal for heavy industry hot surface applications.

This label, the upper surface of which is a 95 µm matte HDPE (high density PE) film, is specific for cold, rough and slightly dirty surfaces. Tree/timber top labels can be given as an example of application. The back scraper of the label is silicon paper. Its total thickness is 202 µm. ( ±10% ISO 534) Quality printing is obtained with thermal transfer resin and wax resin ribbon. The minimum application temperature is 0 °C. The heat resistance after applying is between -20 °C and 70 °C.

This label, which has a white 53 µm PE film on the upper surface, is specially produced for lubricant bottles and oil cans with hot filling application. Adhesive is a new generation emulsion acrylic suitable for such applications. The back scraper is white silicone paper. The total thickness of the label is 166 µm ( ±10% ISO 534). The initial application temperature is at least 0 °C and it is resistant between -20 °C and 0°C during use.

The upper surface of this label, which is called polymide, polyamide, polyimide on the market, is a semi-matte 71 µm polyimide film. Its total thickness is 168 µm. It is heat resistant up to +300°C. It maintains its adhesive strength and does not lose color. Thermal transfer print quality is high. It is UL approved. It has a permanent acrylic adhesive with high heat resistance. It is widely used particularly in electronic circuit boards.